Wet-storage stain

Release time:2022-09-02

Wet storage stain, or white rust, is the term for the white, floury and loose corrosion products shown in below figure. White rust is preferably 

formed on newly galvanized surfaces.

·White rust only forms if there is water(rain or condensation) on the galvanized surfaces, If the galvanized steel are stacked tightly, the attack 

will primarily take place in gaps where ventilation is poor.

·White rust is created due to a corrosion process, that is increased by the fact that there is relatively more oxygen at the edge of a water film 

or a drop of water, than in the middle. A so-called “oxygenation element” is formed because the oxygen-rich areas become nobler cathodes

than the oxygen-poor anodes. 

Such oxidation elements can also cause corrosion on black steel, stainless steel and aluminum.Since this white corrosion product is very 

bulky(about 500times that of the zinc from which it was formed), it can appear to be serious. Though, the white rust is normally not harmful 

to other of the coating’s properties, and the standard for hot-dip galvanizing, EN ISO 1461: 2009, states that white rust is not cause for 

rejection providing the thickness of the zinc coating meets the specified minimum value.

Before the damage has occurred 
The formation of condensation water, which can occur on the galvanized products due to varying temperatures during 

outdoor storage under tarpaulin or equivalent,should therefore also be avoided.
1.Better to be preserved in a ventilated and completely dry conditions.
2.For outdoor storage, the galvanized products should be stacked with wood sloops,make sure there is good air ventilation 

around all surfaces and rainwater can run off all surfaces without accumulation.
3.Outdoor storage which covered with tarpaulin should also be stacked with spacers so that condensate, formed due to 

changing temperature, can be removed by air ventilation. 
4.The covering on galvanized products should therefore only act as a roof that protects against rain and snow,must not 

rest on the galvanized steel and must allow air ventilation.

When the damage has occurred 
The white rust attack can be stopped by removing the moisture on the zinc surface  and will in time be transformed into 

the normal layer of zinc corrosion products, which have a protective effect. 
1. providing adequate air flow to newly galvanized surfaces. 
2. removing standing water from newly galvanized surfaces.
3.Newly formed white rust can often be removed by washing with a stiff nylon brush.
4.White rust that has been on the zinc surfaces for a long time becomes harder and harder to remove. Removal can here 

be done by gentle stainless steel brushing with a cleaning product 
5.Attention to avoid the risk of iron contamination and rust discoloration 
6. A white rust attack that is stopped in time does not need any finishing.